常用塑料原料的收缩率
收缩率系指塑料制品冷却固化经脱模成形后,其尺寸与原模具尺寸间之误差百分比,可依ASTM D955方法测得。在塑料模具设计时,须先考虑收缩率,以免造成成品尺寸的误差,导致成品不良。以下列举几项常用塑料原料之收缩率比较。 热塑性塑料
塑料名称 | 成形收缩率(%) | 塑料名称 | 成形收缩率(%) |
ABS | 0.3~0.8 | PBT | 1.3~2.4 |
AS | 0.2~0.7 | PC | 0.4~0.7 |
CA | 0.3~0.8 | PCTFE | 0.2~2.5 |
CAB | 0.4~0.5 | PE | 0.5~2.5 |
CAP | 1 | PET | 2.0~2.5 |
CP | 0.4~0.5 | PES | 0.5~1.0 |
EC | 0.4~0.5 | PMMA | 0.2~0.8 |
EPS | 0.4 | POM | 0.8~3.5 |
FEP | 3.0~4.0 | PP | 1.0~2.5 |
FRP | 0.1~0.4 | PPO | 0.5~0.7 |
EVA | 0.5~1.5 | PPS | 0.6~1.4 |
HDPE | 1.2~2.2 | PS | 0.2~1.0 |
HIPS | 0.2~1.0 | PVA | 0.5~1.5 |
LCP | 0.1~1.0 | PVAC | 0.5~1.5 |
LDPE | 1.5~3.0 | PVB | 0.5~1.5 |
PA | 0.6~2.5 | 硬质PVC | 0.1~0.5 |
PA-6 | 0.5~2.2 | 软质PVC | 1.0~5.0 |
PA-66 | 0.5~2.5 | PVCA | 1.0~5.0 |
PA-610 | 1.2 | PVDC | 0.5~2.5 |
PA-612 | 1.1 | PVFM | 0.5~1.5 |
PA-11 | 1.2 | SAN | 0.2~0.6 |
PA-12 | 0.3~1.5 | SB | 0.2~1.0 |
PAR | 0.8~1.0 |
塑料名称 | 成形收缩率(%) | 塑料名称 | 成形收缩率(%) |
EP | 0.1~0.5 | SP | 0.0~0.5 |
MF | 0.5~1.5 | UF | 0.6~1.4 |
PDAP | 0.1~0.5 | UP | 0.1~1.2 |
PF | 0.4~0.9 | DAP | 0.1~0.5 |
PU | 0.6~0.8 | BMC | 0.0~0.2 |